Under the normal working condition of the ball mill, the ball mill runs from 720h to 3000h (according to the working conditions, and the specific time is agreed by both the supplier and the buyer). Accumulated the mass of the broken balls during the ball mill operation, call it as the mass. The broken balls […]
Falling-balls test to check the impact fatigue of the grinding balls (Hereinafter referred to falling ball test), under the laboratory condition, simulated the impact process for the grinding balls in the ball mill. Impact times counted by the counter. Impact failure time shows the grinding balls working life in such condition.
The casting grinding ball shall be inspected by the supplier’s quality inspection department. Chemical composition inspection shall be conducted in batches. If melt by induction furnace, each furnace as batch; if melt by cupola furnace, every 2hours as batch. Get one example to inspect the composition for each batch. If the test result is unqualified, […]
6.1 The diameter of the casting grinding ball is measured by a tool with an accuracy of not less than 0.01 mm. 6.2 The analysis method of the chemical composition should be according with the standards of GB/T 223. 3, GB/T 223. 4, GB/T 223.11, GB/T 223. 18, GB/T 223. 23, GB/T 223. 26, GB/T […]
5.1 The grinding balls tolerance of the diameter should be accord with Table 1. 5.2 The main chemical composition of each grades should be accord with Table 2.
4.1 Chrome alloy cast iron grinding balls are divided into 7 grades according to the chrome content. Nodular cast iron grinding balls are divided into two grades according to the matrix structure, I. E. Bainite ductile cast iron grinding balls and Martensite ductile cast iron grinding balls.
GB/T 5611 established and the following terms and attributes shall apply to this standard 3.1 Chrome alloyed cast iron grinding ball The white cast iron with chromium as main alloy element is called chrome alloy cast iron for short, and the cast grinding ball with chrome alloy cast iron as material is called chrome alloy cast iron […]
This standard specifies the product classification, technical requirements, test methods, inspection rules, packaging, marking and transportation of chromium alloy cast iron grinding balls and nodular cast iron grinding balls.
This standard is modified with the USA ASTM A532/A532M-93a (2003) ‘Standard specification for wear-resistant cast iron’ and EU standard EN12513:2000N ‘CAST WEAR-RESISTANT CAST IRON’ and other foreign advanced standards of the relevant provisions.
Add：Heli Technological & Economic Zone,Ningguo City, Anhui Province
China 242300
Tel: 0086-563-4111988
Fax:0086-563-4111988
Phone:0086-15856363380
Email: sara.wu@nghexin.com
sarawu_smart@163.com
Working Time:
Mo - Sa: 8:00 to 21:00
Su:8:00 to 12:00